Tungsten Carbide Rectangular Bars For Woodworking 310mm Carbide Rectangular Strips
Tungsten Carbide Rectangular Bars for Woodworking
| L mm | W mm | T mm | | L mm | W mm | T mm | | L mm | W mm | T mm |
| 310 | 3 | 2 | 310 | 16 | 3 | 310 | 10 | 5 |
| 310 | 4 | 2 | 310 | 18 | 3 | 310 | 12 | 5 |
| 310 | 5 | 2 | 310 | 19 | 3 | 310 | 14 | 5 |
| 310 | 6 | 2 | 310 | 20 | 3 | 310 | 15 | 5 |
| 310 | 7 | 2 | 310 | 22 | 3 | 310 | 16 | 5 |
| 310 | 8 | 2 | 310 | 25 | 3 | 310 | 18 | 5 |
| 310 | 10 | 2 | 310 | 30 | 3 | 310 | 20 | 5 |
| 310 | 12 | 2 | 310 | 32 | 3 | 310 | 22 | 5 |
| 310 | 13 | 2 | 310 | 35 | 3 | 310 | 25 | 5 |
| 310 | 14 | 2 | 310 | 40 | 3 | 310 | 30 | 5 |
| 310 | 15 | 2 | | | | 310 | 35 | 5 |
| 310 | 16 | 2 | 310 | 4 | 4 | 310 | 40 | 5 |
| 310 | 18 | 2 | 310 | 5 | 4 | | | |
| 310 | 19 | 2 | 310 | 6 | 4 | 310 | 6 | 6 |
| 310 | 20 | 2 | 310 | 8 | 4 | 310 | 8 | 6 |
| 310 | 25 | 2 | 310 | 10 | 4 | 310 | 10 | 6 |
| 310 | 30 | 2 | 310 | 12 | 4 | 310 | 12 | 6 |
| 310 | 35 | 2 | 310 | 13 | 4 | 310 | 14 | 6 |
| 310 | 40 | 2 | 310 | 14 | 4 | 310 | 15 | 6 |
| | | | 310 | 15 | 4 | 310 | 16 | 6 |
| 310 | 3 | 3 | 310 | 16 | 4 | 310 | 18 | 6 |
| 310 | 4 | 3 | 310 | 18 | 4 | 310 | 20 | 6 |
| 310 | 5 | 3 | 310 | 20 | 4 | 310 | 25 | 6 |
| 310 | 6 | 3 | 310 | 22 | 4 | 310 | 30 | 6 |
| 310 | 7 | 3 | 310 | 25 | 4 | 310 | 35 | 6 |
| 310 | 8 | 3 | 310 | 30 | 4 | 310 | 40 | 6 |
| 310 | 9 | 3 | 310 | 35 | 4 | | | |
| 310 | 10 | 3 | 310 | 40 | 4 | 310 | 8 | 8 |
| 310 | 12 | 3 | | | | 310 | 10 | 8 |
| 310 | 13 | 3 | 310 | 5 | 5 | 310 | 12 | 8 |
| 310 | 14 | 3 | 310 | 6 | 5 | 310 | 14 | 8 |
| 310 | 15 | 3 | 310 | 8 | 5 | | | |
Tolerance for length +0.20/+1.5
Width: +0/+0.15
Thickness +0/+0.15
Straightness 0.15
Grade K05, with Cobalt: 6%
Tic/Tac: 0.3
Density: 14.94
Hardness: HV30 1650-1750
T.R.S. ≥1560
Grain size: Medium
OED Carbide strips:
Suitable for cutting wooden, metal, plastic, rubber, and so on.
- Advanced formulation manufacturing process,
- Wire cutting
- Anti-corrosion properties of discharge processing
- High-speed stamping resistance
- High wear resistance
Application
Code | Chemical Composition | Physical and mechanical properties
and micro structure as sintered | Application recommended |
| Co | Tic/
Tac | WC | Density | Hardness | Transverse
rupture
strength | Coercivity | Magnetic
saturation | Porosity |
| g/cm3 | HV 30 | N/mm2 | KA/m | % | |
| K05 | 6 | 0.3 | 93.7 | 14.94 | 1650-1750 | ≥1560 | 19.5-24.5 | 5.1-5.9 | A02 B00 | For machining super-hard
grey cast steel, hardening steel, chilled iron, high
silicon-aluminum alloy, high wear-resistant plastic,
hard paper plate and ceramics. |
| 6 | 2 | 92 | 14.95 | 1350-1500 | ≥1600 | 21.5-26.5 | 4.9-5.9 | A02 B00 |
| K10-K15 | 6 | 0.4 | 93.6 | 14.91 | 1665-1835 | ≥123 | 19.5-24.5 | 5.2-6.2 | A02 B00 | For machining cast iron with hardness higher than
200HB, short-chip forgeable cast iron, silicon-aluminum
alloy, copper alloy, plastic, glass, ceramics, and stones. |
| K20 | 6 | 0.4 | 93.6 | 14.9 | 1600-1700 | ≥1670 | 16.3-19.2 | 5.2-6.0 | A02 B00 | For machining grey cast iron with hardness lower than
200HB, non-ferrous metal, copper, brass, and aluminum |
| 7.8 | 1 | 91.2 | 14.61 | ≥1400 | ≥2000 | 15.0-18.0 | 6.6-7.8 | A02 B00 |
| K30 | 6 | 2 | 92 | 14.8 | 1450-1600 | ≥1320 | 13.5-15.1 | 5.3-6.0 | A02 B00 | For machining low-hardness grey cast iron, low-strength
steel and compact wood. |
CIP forming.
CIP Forming can eliminate the internal defects of raw sintered carbide blanks in particular. It can provide uniform density suppression products for the thick carbide strips/plate and special shape carbide products.
Our advantages:
CIP Forming can eliminate the internal defects of raw sintered carbide blanks in particular. It can provide uniform density suppression products for the thick carbide strips/plate and special shape carbide products.
The internal stress can be removed through the cryogenic process to improve the microstructure.
The internal stress can be removed through the vibration process to improve the overall performance.
The service can be improved through the heat treatment process.
Why choose us for carbide wear parts:
- Professional production equipment. From spray drying towers, extrusion molding, mold molding, injection molding, CIP, HIP sintering furnaces, flat grinders, heartless grinders, round grinders, EMD cutting, polishing machines, etc. OED can provide reliable quality assurance for your products.
- The strict control of the production processing. From raw materials, sintering, processing, we will strictly test each process, non-conforming products will not enter the subsequent production.
- Proficient technical team. Senior carbide raw materials engineers: To analyze whether the product meets your application requirements. Senior production managers: To study the most suitable for your product processing methods. Skilled technical inspectors: To test whether the finished product meets your drawing requirements.
- Reliable service. Not only can we provide pre-sales technical services, but our engineers can also come up with product improvements to provide the most reasonable solution for your product.
- Low-cost sample development. For trial orders, such as quantity below 10pcs, our engineer team can help customers to find the solution with mold fees. In this way, our customers can try the samples at a minimized cost.
- Fast delivery. Standard products could be delivered in one week, and the special carbide tools could be finished in 25-45 days after confirming the drawings or 3D model.